Quote:
Originally Posted by Jrainman
the reason why it is not done is the fact of welding two different types of metals is difficult to weld , being SS has very low carbon amounts
it is not that it cant be done but you really have to have good equipment to get good results ,
Tig or brazing would give best results though,
Well there is always the new Ford aluminum body F150
I will say I am not a Ford guy but the paint on those new aluminum body f150 is something to look at , I looked at one at a outdoor show in a dark green and the paint was amazing almost flawless
|
You forgot that the weld is now a mixture of metals and corrosion starts aggressively at the weld line due to electrically dissimilar metals coming together with moisture!